Dental lost wax casting resin-802A
Product Introduction
802A is a specialized wax-up resin material designed for optimal use with Dayoude’s DLP wax-up printer. It is suitable for the production of 3D printed crown wax-ups, bridge wax-ups, and bracket wax-ups. It meets the demands of metal casting processes for removable brackets, posts and cores, and copings, as well as ceramic casting processes such as zirconia crowns, veneers, and inlays.
Specially formulated for dental applications, it is ideal for printing models for dental implants, metal and ceramic crowns, and bridges. Its rapid burnout reduces time and energy consumption during implant manufacturing. The finished model exhibits the highest precision, a crucial requirement in dentistry.
High-Wax Casting Wax Pattern Photosensitive Resin Material:
Product Name: Dental Casting Lost Wax 3D Printing Photosensitive Resin (High-Wax)
Model: 802A
Color: Green, Yellow
Packaging: Bottled
Specifications: 500g/1000g
Compatible Machines: Compatible with DLP reflective light (high light intensity) machines
Light Source Wavelength: Desktop-grade photosensitive resin LED light source with a wavelength of 385nm-405nm
Material Features:
This is a yellow casting material with an 80% wax content, complete combustion, no ash, and low expansion.
The printed wax pattern has clear details and excellent hardness, even tougher than 801.
Supports a variety of paraffin wax casting conditions and is compatible with high-quality gypsum, enhancing the excellent results of jewelry castings using gypsum overlays.
Stronger, more suitable for gold and silver jewelry and dental casting.
Odorless and non-toxic resin. Contains no solvents or irritants. Will not cause allergic reactions. Applications:
Suitable for gold and silver jewelry in the jewelry industry, wax crowns (single crowns, bridges, partial dentures), and steel base wax models in the dental industry, where hardness is a critical factor.
Physical Parameters:
Test Item Test Results
Viscosity 80-150 cps @ 25°C
Critical Exposure Energy 8.1-9.0 mJ/cm²
Tensile Strength 36-52 MPa
Tensile Modulus 1,700-2,335 MPa
Elongation at Break 4-8%
Heat Deflection Temperature 55°C
Shore Hardness 81D
Note:
The above values may vary depending on part geometry, print settings, temperature, and post-curing. Therefore, users must test the product before use to ensure that it meets their end-use performance requirements.
The above values are typical values and are not considered binding material specifications or guarantees unless expressly agreed to in writing. The final results will depend on the user’s actual use. This table is for reference only.
Application Examples: